■ Overview
Chromium-Molybdenum alloy seamlss steel pipes and tubes 12Cr2MoG shall be done Normalized and Tempered heat treatment with Normaling temperature within 900-960 Deg.C and Tempering temperature at 700-750 Deg.C for wall thickness equal or belows 30mm.For pipe wall thickness above 30mm,12Cr2MoG shall be done Quenched and Tempered or Normalized and Tempered.Quenching Temp. above 900 Deg.C,Tempering Temp. 700-750 Deg.C.
■ Full Data
Technical Requirements & Additional Services:
♦ Flattening test according to GB/T 246
♦ Bending test comply to GB/T 232
♦ Flattening test according to GB/T 246
♦ Bending test comply to GB/T 232
♦ Expansion test comply to GB/T 242
♦ Microstructure examination comply to GB/T 13298
♦ Issued Orginal Mill test certificate under 3.1/3.2 FORMAT
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Coating with shop prime
♦ Microstructure examination comply to GB/T 13298
♦ Issued Orginal Mill test certificate under 3.1/3.2 FORMAT
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Coating with shop prime
■ Techicals
►Mechnical property for 12Cr2MoG boiler steel pipes:
|
12Cr2MoG |
|
|
Yield strength (≥Mpa) |
280 |
|
Tensile strength (≥Mpa) |
450-600 |
►Chemical composition for 12Cr2MoG boiler steel pipes (Heat Analysis Max%)
|
Main chemical elements composition of 12Cr2MoG |
|||||
|
C |
Si |
Mn |
P |
S |
Cr |
|
0.08-0.15 |
0.50 |
0.40-0.60 |
0.025 |
0.015 |
2.00-2.50 |
|
Cu |
Ni |
Mo |
V |
Ti |
Zr |
|
0.20 |
0.30 |
0.90-1.13 |
0.08 |
- |
- |