■ Overview
07Cr19Ni10 stainless steel pipes in specification GB/T 5310 shall be done Solution treatment and treatment temperature minimum at 1040 Deg.C and then accelerated colling.Stainless steel pipes grades in GB/T 5310 contains 07Cr19Ni10,10Cr18Ni9NbCu3BN,07Cr25Ni21NbN,
07Cr19Ni11Ti,07Cr18Ni11Nb,08Cr18Ni11NbFG.
07Cr19Ni11Ti,07Cr18Ni11Nb,08Cr18Ni11NbFG.
■ Full Data
Technical Requirements & Additional Services:
♦ Solution Treatment at Min.1040 Deg.C
♦ Flattening test according to GB/T 246
♦ Bending test comply to GB/T 232
♦ Solution Treatment at Min.1040 Deg.C
♦ Flattening test according to GB/T 246
♦ Bending test comply to GB/T 232
♦ Expansion test comply to GB/T 242
♦ Microstructure examination comply to GB/T 13298
♦ Issued Orginal Mill test certificate under 3.1/3.2 FORMAT
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Coating with shop prime
♦ Microstructure examination comply to GB/T 13298
♦ Issued Orginal Mill test certificate under 3.1/3.2 FORMAT
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Coating with shop prime
■ Techicals
►Mechnical property for 07Cr19Ni10 stainless steel pipes:
|
07Cr19Ni10 |
|
|
Yield strength (≥Mpa) |
205 |
|
Tensile strength (≥Mpa) |
515 |
►Chemical composition for 07Cr19Ni10 stainless steel pipes (Heat Analysis Max%)
|
Main chemical elements composition of 07Cr19Ni10 |
|||||||
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Cu |
|
0.04-0.10 |
0.75 |
2.00 |
0.030 |
0.015 |
18.0-20.0 |
8.0-11.0 |
0.25 |