Hot rolled stainless plate 06cr17ni12mo2

Hot rolled stainless plate 06cr17ni12mo2 ( Stainless plate SUS 316) owns good steel plasticity, toughness,cold denatured,welding process performance than stainless plate 06Cr19Ni10 (SUS 304),In high temperature strength,stainless plate SUS 316 is better than stainless sheet SUS 316L,but SUS 316L steel has a better corrosion resistance than SUS 316 because of lower carbon.By adding Molybdenum in chemical composition of stainless sheet 06cr17ni12mo2,these stainless steel materials have good unti-corrosion performance in salts and various inorganic acids and organic acids,alkali while high temperature strength.

Technical Requirements & Additional Services for Hot rolled stainless plate 06cr17ni12mo2:
♦  Ultrasonic examination comply to A578/A578M A577/A577M A435/A435M
♦  Solution treatment or annealing can be done by rapid cooling after heating to 1010-1120°C
♦  Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2 
♦  Bend test shall be complying to GB/T 232
♦  PMI test report,Cutting and welding as per end user’s demands 
♦  Packing,Marking and Mill test certificate format shall be according to GB/T 247

►Mechnical property for stainless sheet 06cr17ni12mo2

stainless plate sus 316
Yield strength (≥Mpa)	Tensile strength (≥Mpa)	Elogation in 50mm min. %	Hardness, Max
			Brinell HBW	Rockwell HRBW
205	515	40	217	95

►Chemical composition for stainless sheet 06cr17ni12mo2 (Heat Analysis Max%)

Main chemical elements composition of stainless plate sus 316
C	Mn	P	S	Si	Cr
0.08	2.00	0.045	0.030	0.75	16.0-18.0
Ni	Mo	N	Cb	Al	Ti
10.0-14.0	2.0-3.0	0.10	-	-	-