A517 Grade F,A517GrF

Pressure vessel A517 Grade F,A517GrF steel plate,A517GrF steel sheet owned high yield strength and tensile strength.For the thickness equal and belows 65mm of High strength steel plate A517GrF,the minimum yield strength should be above 690Mpa,thickness above 65mm,this value shall be 620Mpa.Tensile strength of high strength steel plate A517 Grade F shall be within 795-930Mpa.The additional technical requirements can be choose for ASTM A517 Grade F by our end users,such as Simulated Post-Weld Heat Treatment of Machanical Test Coupons (PWHT),Low temperature Charp V-Notch Impacting Test and High Temperature Tension Test.

Technical Requirements & Additional Services for A517GrF steel plate:
♦ High tension test
♦ Low temperature impacting test
♦ Simulated post-welded heat treatment (PWHT)
♦ Heat treatment under Quenching and Tempering
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Shot blasting and Painting,Cutting and welding as per end user’s demands
♦ Rolling under ASTM A20/A20M for Genenal requirements of pressure vessel used steel 

►Mechnical property for A517GrF steel plate:

Thickness (mm)	Yield strength (≥Mpa)	Tensile strength (Mpa)	Elongation in ≥,%
			50mm
T≤65	690	795-930	16
65<T	620	725-930	14

►Chemical composition for A517GrF steel plate (Heat Analysis Max%)

Main chemical elements composition of A517GrF steel plate
C	Si	Mn	P	S	B	Cr	Ni	V	Mo	Cu
0.10-0.20	0.15-0.35	0.60-1.00	0.035	0.035	0.0005-0.006	0.40-0.65	0.70-1.00	0.03-0.08	0.40-0.60	0.15-0.50