  • A514 Grade R steel plate
  • A514GrR

A514 Grade R,A514GrR

  • Steel Standard: ASTM A514/A514M
  • Rolling Type: High strength steel plate,Quenched and Tempered steel plate
  • Thickness: 6mm-300mm
  • Width: 1500mm-4200mm
  • Length: 3000mm-18000mm
  • Heat Treatment: Quenching and Tempering
(※ Click this button to inquiry)
■ Overview

High strength A514 Grade R,A514GrR,A514GrR steel plate shall be under quenched and tempered.Tension test and Hardness test shall be done in the mill when rolling.All the test result values for structural steel plate A514GrR should write on the original mill test certificate. A514 Grade R is a high strength steel plate with the minimum yield strength at 690Mpa for the thickness belows 65mm,and 620 Mpa for the thickness above 65mm,the tensile strength shall be within 760-895 Mpa. The manufacturer may reheat-treat plates that fail to meet the mechanical property requirements of this specification when rolling of high tension steel plate A514GrR.

■ Full Data
Technical Requirements & Additional Services for A514GrR steel plate:
♦ High tension test
♦ Low temperature impacting test
♦ Simulated post-welded heat treatment (PWHT)
♦ Heat treatment under Quenching and Tempering
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Shot blasting and Painting,Cutting and welding as per end user’s demands
♦ Rolling under ASTM A6/A6M for Genenal requirements of structural used steel 
■ Techicals

Mechnical property for A514GrR steel plate:

Thickness (mm) Yield strength (≥Mpa) Tensile strength (Mpa) Elongation in ≥,%
  50mm
T≤65 690 760-895 18
65<T 620 690-895 16

Chemical composition for A514GrR steel plate (Heat Analysis Max%)

Main chemical elements composition of A514GrR steel plate
C Si Mn P S Ti Cr Mo Ni
0.15-0.20 0.20-0.35 0.85-1.15 0.035 0.035 0.03-0.08 0.35-0.65 0.15-0.25 0.90-1.10