HOT ROLLED STAINLESS PLATE A240 434

Comparasion with stainless steel plate A240 431,stainless steel plate A240 434 added Mo within 0.75-1.25% but no requirement of minimum Ni % in chemical composition.Yeild strength shall be determined by the offset method at 0.2% in accordance wtih the test methods and definitions A370.

Technical Requirements & Additional Services for HOT ROLLED STAINLESS PLATE A240 434:
♦  Ultrasonic test according to ASTM A578,A577 or A435
♦  Definiations for Mechanical testing comply to A370
♦  Test Methods,Practices and Terminology for chemical analysis comply to A751
♦  Practices for detecting susceptibility to Intergranular corrosion in Austenitic stainless steels
♦  Packing with water-resistance paper and Non-fumigation wooden crates
♦  Paper Interleave,Polyethylene Film coating （PE COAT）for cold rolled stainless steels

►Mechnical property for Stainless steel sheet A240 TP434

Stainless steel plate a240 434
Yield strength (≥Mpa)	Tensile strength (≥Mpa)	Elogation in 50mm min. %	Hardness, Max
			Brinell HBW	Rockwell HRBW
240	450	22	-	89

►Chemical composition for Stainless steel sheet A240 TP434 (Heat Analysis Max%)

Main chemical elements composition of Stainless steel plate a240 434
C	Mn	P	S	Si	Cr
0.12	1.0	0.040	0.030	1.0	16-18
Ni	N	Al	Ti	Al	Cu
-	0.75-1.25	-	-	-	-