HOT ROLLED STAINLESS STEEL PLATE A240 304H

HOT ROLLED STAINLESS STEEL PLATE A240 304H with UNS Designation S30409,hot rolled with annealed heat treament at temperature above 1040 ℃ and Pickled.Stainless steel sheet A240 TP304H No.1 is a dull,non-reflective finish.Thickness tolerance shall be completely consistent with speicifcation A480 / A480M.

Technical Test Method for HOT ROLLED STAINLESS STEEL PLATE A240 304H:
♦  Ultrasonic test according to ASTM A578,A577 or A435
♦  Grain sizes test according to ASTM E112
♦  Definiations for Mechanical testing comply to A370
♦  Test Methods,Practices and Terminology for chemical analysis comply to A751
♦  Practices for detecting susceptibility to Intergranular corrosion in Austenitic stainless steels

Additional Services for Stainless steel sheet A240 TP304H:
♦  PMI test report,Cutting and welding as per end user’s demands 
♦  Packing with water-resistance paper and Non-fumigation wooden crates
♦  Paper Interleave,Polyethylene Film coating （PE COAT）for cold rolled stainless steels

►Mechnical property for Stainless steel sheet A240 TP304H

Austenitic stainless steel plate 304H
Yield strength (≥Mpa)	Tensile strength (≥Mpa)	Elogation in 50mm min. %	Hardness, Max
			Brinell HBW	Rockwell HRBW
205	515	40	201	92

►Chemical composition for Stainless steel sheet A240 TP304H (Heat Analysis Max%)

Main chemical elements composition of Austenitic stainless steel plate 304H
C	Mn	P	S	Si	Cr
0.04-0.10	2.00	0.045	0.030	0.75	18.0-20.0
Ni	N	Cu	Mo	Al	Ti
8.0-10.5	-	-	-	-	-